Electrochemical Properties of TiAl-Based Alloys
Künye
Crossmark. (2023). Retrieved March 5, 2024, from Crossref.org website: https://crossmark.crossref.org/dialog/?doi=10.1134/S0031918X23600586 Özet
Abstract: TiAl alloys represent a promising potential for use in many fields including automotive, aerospace and marine industries. Therefore, it can be considered important to investigate the ability of these alloys to withstand such harsh environments. To this intended, the following study attempted to determine the electrochemical properties of Ti–48Al–2Mo–2(Cr,Mn) (at %) alloys in 3.5 wt % NaCl solution. The results of potentiodynamic polarization experiment revealed that Mo addition can enhance the corrosion resistance of the alloys, especially the Ti–48Al–2Cr alloy. Ti48Al–2Cr–2Mo was found to have the lowest corrosion rate value of 0.1153 mm/year, whereas Ti48Al–2Mn was found to have the highest corrosion rate value of 0.3952 mm/yr. The polarization resistance (R p) of the alloys changes from 1.33 to 5.54 kΩ cm2 depending on alloyed compositions. The electrochemical impedance spectroscopy (EIS) results confirmed that the corrosion behavior can be tailored through Mo addition. Accordingly, the best corrosion resistance belongs to the Ti48Al–2Cr–2Mo alloy, which presents the highest impedance value of 4.98 × 103 Ω. The surface morphologies of corroded alloys exhibited the pitting corrosion characteristics after the polarization experiments in 3.5 wt % NaCl solution. The number density of corrosion pits was significantly higher on the surfaces of the Ti48Al–2Mn and Ti48Al–2Mn–2Mo alloys. The enhanced corrosion resistance of Ti48Al–2Cr–2Mo alloy to NaCl solution is believed to be associated with the coupled positive effect of Cr and Mo in forming a surface film with a good protective ability. In addition, Ti48Al–2Cr–2Mo exhibited high resistance to NaCl solution at a level, which can be considered an optimum material for fabricating parts that serve in the marine environment. © 2023, Pleiades Publishing, Ltd.
WoS Q Kategorisi
Q3Kaynak
Physics of Metals and MetallographyKoleksiyonlar
İlgili Öğeler
Başlık, yazar, küratör ve konuya göre gösterilen ilgili öğeler.
-
An investigation on the corrosion performance of Fe(2)CoCrNi(0.5 )based high entropy alloys
Garip, Yigit (Pergamon-Elsevier Science Ltd, 2022)The electrochemical and hot corrosion behaviors of Fe2CoCrNi0.5 based HEAs were investigated. The HEA with the best electrochemical corrosion resistance was Fe2CoCrNi0.5Si0.25Cu0.25 with Ecorr of - 0.584 V, Icorr of 1.47 ... -
Corrosion behavior of the resistance sintered TiAl based intermetallics induced by two different molten salt mixture
Garip, Yiğit; Özdemir, O. (Elsevier Ltd, 2020)The cyclic hot corrosion behaviors of TiAl based intermetallics were studied in two different molten salts consisting of % wt. Na2SO4-25NaCl and Na2SO4-25K2SO4 at 800 and 900 °C for 180 h, respectively. The aim of the study ... -
Prediction modeling of Type-I hot corrosion performance of Ti–Al–Mo-X (X=Cr, Mn) alloys in (Na, K)2SO4 molten salt mixture environment at 900°C
Garip, Yiğit; Garip, Zeynep B.; Özdemir, O. (Elsevier Ltd, 2020)The aim of this study was to investigate the Type-I hot corrosion performance of Ti–48Al–1Mo–2Cr and Ti–48Al–1Mo–2Mn (at.%) alloys in the Na2SO4–25K2SO4 (wt.%) molten salt environment at 900C for 180 h under cyclic conditions, ...