Effect of coating degradation on the hot corrosion behavior of yttria-stabilized zirconia (YSZ) and blast furnace slag (BFS) coatings
Künye
Karaoglanli, A. C., Ozgurluk, Y., Gulec, A., Ozkan, D., & Binal, G. (2023). Effect of coating degradation on the hot corrosion behavior of yttria-stabilized zirconia (YSZ) and blast furnace slag (BFS) coatings. Surface and Coatings Technology, 473, 130000. https://doi.org/10.1016/j.surfcoat.2023.130000 Özet
In order to provide thermal insulation thermal barrier coatings (TBCs) used in gas turbine engine components under conditions of impure fuels and high turbine inlet temperatures are expected to have hot corrosion resistance. Techniques and material combinations used in the production of TBCs are primarily effective in the progression of failure mechanisms as a result of hot corrosion. In this study, the hot corrosion damage mechanism, which is caused by the impurities of the fuels used in the industry and causes great damage to the TBC systems, was simulated and evaluated in the laboratory environment. For the creation of TBC systems, CoNiCrAlY metallic bond coating powders were deposited on Ni-based super alloy substrates by the detonation gun (D-gun) process. Commercial yttria-stabilized zirconia (YSZ) and blast furnace slag (BFS) powders were deposited on the bond coating by Atmospheric plasma spraying (APS) technique. Hot corrosion testing of TBCs was performed at 800 °C for 8, 24, 50, and 75 h in an environmental condition consisting of a 45 wt% Na2SO4 and 55 wt% V2O5 corrosive salt mixture. Blast furnace slag, which is completely cost-free and a waste product, provided excellent protection against hot corrosion damage without deteriorating its stability at high temperatures. In this way, it is open to be evaluated as a new type of coating material alternative to the traditional top coating material YSZ, which has a very high production and cost, and to be used in different areas. © 2023 Elsevier B.V.
WoS Q Kategorisi
Q1Kaynak
Surface and Coatings TechnologyCilt
473Koleksiyonlar
İlgili Öğeler
Başlık, yazar, küratör ve konuya göre gösterilen ilgili öğeler.
-
Evaluation of fracture toughness and crack propagation of aluminum alloy 7075–T651 with chromium oxide coating
Altuncu, Ekrem; Irıc, S. (Polish Academy of Sciences, 2019)Fatigue crack formation is the most important factor affecting the damage in parts under subjected to the repeated stresses. In this context, intensive researches are continuing on the protective hard coatings in the ... -
Prediction modeling of Type-I hot corrosion performance of Ti–Al–Mo-X (X=Cr, Mn) alloys in (Na, K)2SO4 molten salt mixture environment at 900°C
Garip, Yiğit; Garip, Zeynep B.; Özdemir, O. (Elsevier Ltd, 2020)The aim of this study was to investigate the Type-I hot corrosion performance of Ti–48Al–1Mo–2Cr and Ti–48Al–1Mo–2Mn (at.%) alloys in the Na2SO4–25K2SO4 (wt.%) molten salt environment at 900C for 180 h under cyclic conditions, ... -
Corrosion behavior of the resistance sintered TiAl based intermetallics induced by two different molten salt mixture
Garip, Yiğit; Özdemir, O. (Elsevier Ltd, 2020)The cyclic hot corrosion behaviors of TiAl based intermetallics were studied in two different molten salts consisting of % wt. Na2SO4-25NaCl and Na2SO4-25K2SO4 at 800 and 900 °C for 180 h, respectively. The aim of the study ...