TRIBOLOGICAL PERFORMANCE OF Ni-W/PTFE COMPOSITE COATING VIA PULSE ELECTRODEPOSITION
Özet
The Ni-W/PTFE co-depositions were successfully prepared on steel via pulse electrodeposition methods. Electrodeposition was perform by dispersing 5-20 g/L PTFE particles from Ni-Watt bath. The surface morphology, phase analyses crst-alytallite size, distorsion and hardness of the samples were characterized by SEM, XRD, and Vicker???s microhardness tester. The friction coefficient of the coatings were carried out using CSM microtester. As increasing with the concentration of the PTFE in the solution, the wear resistance properties of theco-depositions were increased. These experimental results determined that the PTFE concentration of 15 g/L in the electrolyte was the optimum content to obtain the best micro-structure and wear performance.